Our structural steel subcontractor is currently using a Sherwin Williams Weld-Thru Primer at the shop location. This is for anti-corrosive/rust purposes. I don't have to include this product as part of this credit, correct?
You rely on LEEDuser. Can we rely on you?
LEEDuser is supported by our premium members, not by advertisers.
Go premium for
Glen Phillips
Sustainability ProfessionalBright Green
42 thumbs up
March 14, 2017 - 2:31 pm
The VOC requirements for NC 2009 apply to only site-applied coatings, so unless their shop is located inside the LEED project, it would be exempt.
Jon Clifford
LEED-AP BD+CGREENSQUARE
LEEDuser Expert
327 thumbs up
March 17, 2017 - 7:12 pm
When I encounter a shop-applied coating or primer, for steel or any other substrate, I always ask what product will be used if the shop coat gets damaged and requires on-site touch-up after delivery or installation. This situation is common for steel fabrications where welds, mechanical fasteners, or field modification must be re-primed on-site.
Many specifications say to use the same product for on-site touch-up as was applied in the shop. In such cases, I include the shop coating in the IEQc4.2 documentation. If one of these shop coats doesn’t meet the VOC limits, I work with the design team and the contractor to find a compatible compliant repair product to use for on-site touch-up.
Jason Biondi
Managing DirectorEnergy Cost Solutions Group
17 thumbs up
March 19, 2017 - 9:58 pm
Yes, when these welded surfaces are re-primed, one needs to include "Structural Steel primer" for IEQc4.2.
You can document/qualify this coating as "Anti-Corrosive/ Anti-Rust Paint", the VOC limit will be 250 g/l;
In our experience, we have found that Sherwin-Williams metal primer products are SCAQMD compliant.